The grinders that try to induction harden those Cummins cams back to spec are pissin up a rope. Just an opinion, of course.
I will bite,
Can you elaborate on this please?
The grinders that try to induction harden those Cummins cams back to spec are pissin up a rope. Just an opinion, of course.
I will bite,
Can you elaborate on this please?
The material used is 3D Ductile iron. It cant be flame or induction hardened by its alloy design. It is designed to be poured into a chilled mold. I would rather leave rehardening to someone dumber than me, smarter than me, or luckier than me to try and make work.
Some ductile irons can be induction hardened.
RonA,
You are right.
Im callin' the cops, Racin is using the race card. LMFAO!!
From the bottom of the deck too. LOL
:hehe::hehe::hehe::hehe:So sorrie!!Im callin' the cops, Racin is using the race card. LMFAO!!
From the bottom of the deck too. LOL
Can this cam thread please not be flushed down the pooper ya'll? There are some people like myself who like trying to learn about these things....